Electrochemical lithiation of the binary compound TiSb.
Автор(и)
V. M. Kordan
Ivan Franko National University of Lviv
T. А. Fedak
Ivan Franko National University of Lviv
I. I. Tarasiuk
Ivan Franko National University of Lviv
O. Ya. Zelinska
Ivan Franko National University of Lviv
V. V. Pavlyuk
Ivan Franko National University of Lviv
Анотація
The sample with the composition Ti50Sb50 was synthesized by arc melting of the pressed mixture of pure metals with further annealing in evacuated silica tube at 400 oC for two months. The X-ray phase analysis (diffractometer DRON-2.0M, Fe Kα-radiation) confirmed the formation of TiSb (structure type NiAs, space group P63/mmc) as a major phase and negligible amount of antimony as a minor phase.
Біографії авторів
V. M. Kordan, Ivan Franko National University of Lviv
Department of Inorganic Chemistry
T. А. Fedak, Ivan Franko National University of Lviv
Department of Inorganic Chemistry
I. I. Tarasiuk, Ivan Franko National University of Lviv
Department of Inorganic Chemistry
O. Ya. Zelinska, Ivan Franko National University of Lviv
Department of Inorganic Chemistry
V. V. Pavlyuk, Ivan Franko National University of Lviv